corrosion cracking的例句大全

Influence of Some Processing Factors on Susceptibility to Caustic Stress Corrosion Cracking of Modified Alloy 800

某些加工因素对改性800合金碱性应力腐蚀破裂敏感性的影响

Effect of cold work on the caustic stress corrosion cracking of alloy 800

冷加工对800合金抗碱性应力腐蚀破裂的影响

With an increase of the chromium content in the cast steel, active dissolving corrosion increased, however, tendency of caustic embrittlement cracking decreased.

随着钢中含铬量的增加，试验材料的活性溶解腐蚀失重增大，但碱脆开裂的倾向减少。

All planes are being inspected for possible cracking and corrosion.

所有的飞机都在接受检查，看是否可能有裂纹和腐蚀现象。

Corrosion Fatigue Cracking of In-service 4340 Steel Super High Pressure Pipe

在役4340钢超高压管的腐蚀疲劳开裂

Acid alkaline, corrosion-resistant, non-cracking, Health and pests, weathering strong.

耐酸碱 、 耐腐蚀 、 不龟裂 、 不生虫害, 耐候性强.

The test and analysis conclude that the cracking failure of minimum flow by-pass line of high-pressure lean amine pump in the hydrocracker are caused by sulfur stress corrosion and turbulent flow corrosion, which are aggravated by pipeline vibration.

经过检测分析认为加氢裂化装置高压贫胺液泵最小流量控制阀副线的腐蚀开裂原因是胺液和硫化氢的应力腐蚀和湍流腐蚀，管线振动加剧了腐蚀。

The results show that no stress corrosion cracking in U shape samples is found and average static uniform corrosion rate is less than 2 mg/ dm 2 after testing in high temperature borated water for 5 000 h.

试验结果表明：在高温含B水中，U型试样试验5000h后无应力腐蚀破裂，静态月平均腐蚀速率小于2mg/dm2。

Sulfur Hydrogen Corrosion Cracking and Prevention Measures of the CNG Steel Cylinders

CNG储气瓶的硫化氢腐蚀破裂及预防措施

The results showed that extensive dezincification occurred in all the tests but potential had opposite effects on the dezincification coefficient and susceptibility to stress corrosion cracking; an increase in potential accelerated crack velocity but depressed the dezincification coefficient.

结果表明，所有试验都发生严重脱锌，但是，电位对脱锌系数和应力腐蚀开裂敏感性的作用影响相反：提高电位加速裂纹扩展，却降低了脱锌系数。

The results showed that the corrosion weight loss rate of high Mn steel was distinctly greater than that of medium carbon chromium steel. The high Mn steel caustic embrittlement cracking was distinct in corrosion.

结果表明，高锰钢的平均腐蚀速率显著高于中碳铬合金钢，腐蚀过程中高锰钢有较严重的碱脆开裂现象。